135℃ EPDM Elastomer Irradiation-Crosslinkable Insulation Compound

135℃ EPDM Elastomer Irradiation-Crosslinkable Insulation Compound

135℃ EPDM Elastomer Irradiation-Crosslinkable Insulation Compound is mainly formulated with modified EPDM rubber as the base polymer, compounded with various additives. Through mixing and extrusion pelletization processes, it achieves exceptional processability, physical-mechanical properties, and electrical insulation performance. Cables manufactured with this material develop a smooth, rounded surface with superior elasticity and tactile quality after irradiation crosslinking. It is suitable for magnet wires, control cables.

135℃ EPDM Elastomer Irradiation-Crosslinkable Insulation Compound List

Model	Unit	238E
Item	/	Typical
Density	g/cm3	1.02
Tensile Strength	MPa	9.4
Elongation at Break	%	470
Air Oven Aging	℃×h	165×168
Tensile Strength Change Rate	%	-13
Elongation at Break Change Rate	%	-11
Hot Set (0.2MPa)	℃×min	250×15
Elongation under Load	%	40
Permanent Deformation after Cooling	%	1
Low-temperature Performance Test	℃	-45
Ozone Resistance Test	/	No cracking
Volume Resistivity at 20°C	Ω·cm	5.8×1014
Dielectric Strength at 20°C	kV/mm	27
Oxygen Index	%	/
Cable Flame Retardancy	/	/
Smoke Density: Smoke with flame (Dmy)	/	/
Smoke without flame (Dmw)	/	/
Halogen Acid Gas Content	mg/g	/
pH Value	/	/
Conductivity	μs/mm	/
Toxicity Index	/	/
Environmental Protection Requirements	Level	Conforms to EU RoHS Directive (2011/65/EU) and REACH Regulation (EC 1907/2006) Substances of Very High Concern (SVHC) provisions.

135℃ EPDM Elastomer Irradiation-Crosslinkable Insulation Compound Application

135℃ EPDM Elastomer Irradiation-Crosslinkable Insulation Compound achieves exceptional processability, physical-mechanical properties, and electrical insulation performance. It is suitable for magnet wires, control cables.