150℃ Irradiation-Crosslinkable Polyolefin Insulation Compound

150℃ Irradiation-Crosslinkable Polyolefin Insulation Compound

150℃ Irradiation-Crosslinkable Polyolefin Insulation Compound is formulated with modified polyethylene resin as the base material, combined with various additives. This material features excellent extrusion processability, superior physical-mechanical properties, and high-temperature resistance. Additionally, it offers outstanding high-voltage endurance and cut-through resistance. It is primarily suitable for thin-wall, high-voltage insulated cables.

150℃ Irradiation-Crosslinkable Polyolefin Insulation Compound List

Model	Unit	250E
Item	/	Typical
Density	g/cm3	0.93
Tensile Strength	MPa	17.0
Elongation at Break	%	450
Air Oven Aging	℃×h	180×168
Tensile Strength Change Rate	%	-1
Elongation at Break Change Rate	%	-7
Hot Set (0.2MPa)	℃×min	200×15
Elongation under Load	%	45
Permanent Deformation after Cooling	%	1
Low-temperature Performance Test	℃	-45
Low-temperature Impact Brittleness Temperature	℃	-76
Ozone Resistance Test	/	No cracking
4-hour AC Voltage Withstand Test	kV	/
Volume Resistivity at 20°C	Ω·cm	5.8×1015
Dielectric Strength at 20°C	kV/mm	28
Environmental Protection Requirements	/	Conforms to EU RoHS Directive (2011/65/EU) and REACH Regulation (EC 1907/2006) Substances of Very High Concern (SVHC) provisions.

150℃ Irradiation-Crosslinkable Polyolefin Insulation Compound Application

150℃ Irradiation-Crosslinkable Polyolefin Insulation Compound features excellent extrusion processability, superior physical-mechanical properties, and high-temperature resistance. It is suitable for the following applications:
1. Power cables;
2. Control cables.