125℃ Halogen-Free Irradiation-Crosslinkable Polyolefin Insulation Compound

125℃ Halogen-Free Irradiation-Crosslinkable Polyolefin Insulation Compound

125℃ Halogen-Free Irradiation-Crosslinkable Polyolefin Insulation Compound is formulated with modified polyethylene resin as the base material, combined with various additives. This material features high resistivity, thin-wall insulation, crack resistance at -65°C, high temperature resistance, and other superior characteristics. It is primarily suitable for control cables, locomotive cables.

125℃ Halogen-Free Irradiation-Crosslinkable Polyolefin Insulation Compound List

Model	Unit	225-65E
Item	/	Typical
Density	g/cm3	0.95
Tensile Strength	MPa	18.4
Elongation at Break	%	700
Air Oven Aging	℃×h	158×168
Tensile Strength Change Rate	%	-9
Elongation at Break Change Rate	%	-15
Hot Set (0.2MPa)	℃×min	200×15
Elongation under Load	%	55
Permanent Deformation after Cooling	%	0
Low-temperature Performance Test	℃	-65
Low-temperature Impact Brittleness Temperature	℃	-76
Ozone Resistance Test	/	No cracking
4-hour AC Voltage Withstand Test	kV	/
Volume Resistivity at 20°C	Ω·cm	7.8×1015
Dielectric Strength at 20°C	kV/mm	29
Environmental Protection Requirements	/	Conforms to EU RoHS Directive (2011/65/EU) and REACH Regulation (EC 1907/2006) Substances of Very High Concern (SVHC) provisions.

125℃ Halogen-Free Irradiation-Crosslinkable Polyolefin Insulation Compound Application

125℃ Halogen-Free Irradiation-Crosslinkable Polyolefin Insulation Compound features high resistivity, thin-wall insulation, crack resistance at -65°C, high temperature resistance, and other superior characteristics. It is suitable for the following applications:
1. Control cables;
2. Locomotive cables.