150℃ LSHF/LSZH Flame-Retardant Irradiation-Crosslinkable Polyolefin Insulation Compound

150℃ LSHF/LSZH Flame-Retardant Irradiation-Crosslinkable Polyolefin Insulation Compound

150℃ LSHF/LSZH Flame-Retardant Irradiation-Crosslinkable Polyolefin Insulation Compound is mainly made of halogen-free non-toxic modified polyolefin resin as the main raw material, with the addition of environmentally friendly flame retardants, heat stabilizers, smoke suppressants, mold inhibitors and other additives. It is produced through mixing, extrusion, and granulation. This material has good processing performance, physical and mechanical properties, insulation performance, and excellent flame retardant properties. It does not release halogen acid and self extinguishes upon ignition, which can greatly reduce the emission of toxic and corrosive gases and the generation of smoke. After immersion in water, the insulation resistance changes little, and it has high safety and reliability when made into cables.

150℃ LSHF/LSZH Flame-Retardant Irradiation-Crosslinkable Polyolefin Insulation Compound List

Model	Unit	150E	150E-1	150E-2	150-6	157-6
Item	/	Typical	Typical	Typical	Typical	Typical
Density	g/cm3	1.55	1.46	1.36	1.46	1.48
Tensile Strength	MPa	13.1	13.2	15.2	12.9	13.1
Elongation at Break	%	265	250	328	265	253
Air Oven Aging	℃×h	180×168	180×168	180×168	180×168	180×168
Tensile Strength Retention Rate	%	97	98	96	-2	-2
Elongation Retention Rate	%	82	86	85	-14	-12
Hot Set (0.2MPa)	℃×min	200×15	200×15	200×15	200×15	200×15
Elongation under Load	%	85	89	95	89	85
Permanent Deformation after Cooling	%	5	4	3	4	3
Heat Deformation Test (UL1581)	℃×h	121×1	121×1	121×1	/	/
Deformation Rate	%	18	20	19	/	/
Thermal Shock (per UL1581)	℃×h	121×1	121×1	121×1	/	/
Test Results	/	No cracking	No cracking	No cracking	/	/
Low-temperature Impact Brittleness Temperature	℃	-40	-45	-45	-45	-45
Ozone Resistance Test	/	No cracking	No cracking	No cracking	No cracking	No cracking
Volume Resistivity at 20°C	Ω·cm	5.6×1014	8.9×1014	9.1×1014	5.4×1014	2.2×1015
Dielectric Strength at 20°C	kV/mm	28	29	27	26	28
Oxygen Index	%	33	31	30	32	30
Cable Flame Retardancy	/	VW-1	DZ-1	FT2	/	/
Smoke Density: Smoke with flame (Dmy)	/	65	51	63	51	48
Smoke without flame (Dmw)	/	132	134	125	134	136
Halogen Acid Gas Content	mg/g	0	0	0	0	0
pH Value	/	5.3	5.9	6	5.9	5.9
Conductivity	μs/mm	1.1	0.9	1.1	0.9	1.1
Toxicity Index	/	2.1	1.9	2	1.9	1.8
Smoke Toxicity Hazard Classification	Level	/	/	/	ZA2	ZA2

150-6 &157-6 are non environmentally friendly products.
150E, 150E-1 & 150E-2 are environmentally friendly products. These eco-friendly insulation materials comply with:
EU RoHS Directive (2002/95/EC) requirements;
15 Substances of Very High Concern (SVHC) under EU REACH Regulation (1907/2006);
SONY SS-00259 (13th Edition) standards.

150℃ LSHF/LSZH Flame-Retardant Irradiation-Crosslinkable Polyolefin Insulation Compound Application

150℃ LSHF/LSZH Flame-Retardant Irradiation-Crosslinkable Polyolefin Insulation Compound has good processing performance, physical and mechanical properties, insulation performance, and excellent flame retardant characteristics. It is mainly used as an insulation material for the production of control cables, instruments, meters, signal cables, electronic wires, and other cables.